Ribbon bonding in an electronic package

ABSTRACT

A flexible conductive ribbon is ultrasonically bonded to the surface of a die and terminals from a lead frame of a package. Multiple ribbons and/or multiple bonded areas provide various benefits, such as high current capability, reduced spreading resistance, reliable bonds due to large contact areas, lower cost and higher throughput due to less areas to bond and test.

CROSS REFERENCE TO RELATED APPLICATIONS

This is a continuation application of U.S. patent application Ser. No.11/675,534, filed Feb. 15, 2007, which is a divisional application ofU.S. patent application Ser. No. 10/429,128, filed May 2, 2003, nowabandoned.

BACKGROUND

1. Field of the Invention

The present invention relates to semiconductor devices, and inparticular, to interconnecting a semiconductor die to a terminal lead ina semiconductor package.

2. Related Art

In the manufacture of semiconductor devices, active elements in asemiconductor device, such as drain and/or source regions in asemiconductor die, are electrically connected to other devices orelectronic components, such as on a printed circuit board. However,since semiconductor devices can be susceptible to environmentalconditions, such as dust, moisture, and sudden impact, which can damageor otherwise interfere with the proper operation of the device, thedevice is typically protected by a die package. The die package bothprotects the die and allows the die to electrically connect to externaldevices. To facilitate the latter, specific portions of the die areelectrically coupled to external leads of the package or lead frame,such as with bond wires or solder balls.

FIG. 1 shows a side view of a typical connection between a powersemiconductor die 10 (e.g., a MOSFET) and part of a lead frame 12. Leadframe 12 includes a lead 14 and a die pad 16. Lead 14 allows die 10 toelectrically couple external elements after die 10 is connected. Die 10is mounted on or secured to die pad 16. The upper surface of die 10includes a metalized portion 22, such as aluminum, that provides contactwith underlying active elements of die 10. An electrical connection isthen made between metalized portion 22 and contact portion 18.Typically, the connection is made by bonding, e.g. ultrasonicallybonding, a conductive wire 24 between the two portions. Materials forwire 24 include gold, aluminum, and copper. FIG. 1 shows a single bond,connection, or stitch 26 between wire 24 and metalized portion 22.

The amount of current flow from die 10 to lead 14 depends, in part, onthe total resistance in the current path, as shown by the arrows inFIG. 1. This resistance is due, in part, to the resistance of wire 24and the spreading resistance along metalized portion 22. The spreadingresistance increases as the distance the current has to travel from themetalized portion to the stitch increases. The spreading resistance alsoincreases as the thickness of metalized portion 22 decreases. Typicalmetalization thickness is in the range of approximately 3 to 5 microns(i.e., much smaller than the wire thickness). It is desirable to lowerthe overall electrical resistance of the connections, especially to keeppace with the intrinsic resistance of the semiconductor die, which iscontinuously decreasing. However, increasing the thickness of metalizedportion 22 also increases the cost by decreasing throughput of thewafer/die manufacturing process.

Further, wires are limited by their size, typically around 20 mil indiameter, which also limits the amount of current that can be carried ineach wire. Consequently, large numbers of wires are sometimes needed tomake the desired connections in certain applications, which can increasethe cost and decrease throughput of the interconnect process equipment(e.g., the wire bonder).

Instead of wires, other types of bonding utilize a strap to connect thedie to the lead frame. One such configuration is shown in FIG. 2 and isdisclosed in U.S. Pat. No. 6,040,626, entitled “Semiconductor Package”,issued to Cheah et al. A single conductive strap 50, e.g., copper, isused to obtain an electrical connection between metalized portion 22 ondie 10 and lead 14 of the package/module. Strap 50 can be eithersoldered or glued to two contact areas 52 and 54, such as with anelectrically conductive epoxy or solder paste 56. Use of a strapprovides the advantages of reducing resistance to current flow byproviding a large contact area for coupling metalized portion 22 to lead14, e.g., spreading resistance is greatly reduced.

However, using a strap also has disadvantages. In order to solder strap50 to the surface of metalized portion 22, a solderable metalization,e.g., copper or nickel, is required. In general, such a metalizationrequires a stack of several different metal layers (not shown), witheach layer having a specific function, e.g., adhesion, barrier, andsolderability, of the soldering process. These layers, which aredifferent than the standard metalization layer, e.g., aluminum, togetherresult in higher manufacturing cost of the metalization, andconsequently of the semiconductor die. Typically, a solder paste processis applied to join the parts. Solder paste 56 contains some type of fluxcomponent, which is required to (1) temporarily tack the components, (2)protect them from oxidizing (especially if the reflow process takesplace in air), and (3) remove/reduce oxides already present. Dependingon the quality of the parts, only the use of a strong flux provides arobust process and reliable result of the soldering process. It is wellknown that flux residues cover the surfaces after reflow. Beside othernegative effects (like corrosion in contact with humidity), theirpresence negatively influences the strength and reproducibility of theadhesion of the molding compound in a subsequent package encapsulation.This again can result in a limited reliability of such parts. As aconsequence, parts processed with solder paste typically need to bethoroughly cleaned after reflow and before further processing/packaging.

However, cost effective wet chemical cleaning processes are known tooffer limited process control capability, causing an increased yieldloss potential, beside the additional costs (e.g., labor, floor space,equipment, consumables, and yield loss) due to the need for thisadditional process step. Such a cleaning is also difficult to automate(which would reduce labor cost) and difficult to implement in a cleanroom environment. Furthermore, wet chemical processes, as well as solderreflow using flux (fumes), may be environmentally unfriendly. Two otherdisadvantages of a copper strap interconnect are (1) limited flexibility(since the straps are typically stamped on the die bonder, devicechanges which require a different strap geometry will require exchangingthe stamping tool, which increases time and cost) and (2) the relativelystiff copper strap can form a significant stress on the silicon die,which can cause the die to crack, especially if the thickness of theattachment layer (e.g., solder or epoxy) is not well controlled above acertain minimum.

Another type of interconnect currently used is a solder ball basedinterconnect, such as disclosed in U.S. Pat. No. 6,442,033, entitled“Low-cost 3D Flip-chip packaging technology for integrated powerelectronics modules”, issued to Liu Xingsheng et al., and in U.S. Pat.application publication No. US 2002/0066950, entitled “Flip chip inleaded molded package with two dice”, by Rajeev Joshi, both of which areincorporated by reference in their entirety. Solder ball basedinterconnects have similar disadvantages to those of the strapconfiguration with regards to the use of solder paste and inflexibility.In high current applications, such a configuration has the additionaldisadvantage of the solder's high susceptibility to electromigration.

Thus, it is highly desirable to use a clean, environmentally friendlyprocess, which can be well controlled, as well as a flexibleinterconnect. The ultrasonic bonding process is one such process.However, it is also desirable to reduce the number of connections, inorder to increase the production rate of existing equipment, and reducethe cost of manufacturing. Furthermore, it is desirable to improve theelectrical performance of connections, which would require eitherreducing the electrical resistance and/or increasing the currentcapability, depending on the type of application. Especially fordiscrete semiconductor devices, it is also desirable to reduce theoverall size of a device, and therefore the volume required by theconnection.

Accordingly, there is a need for an improved type of connectionprocessed using ultrasonic bonding, which overcomes the deficiencies inthe prior art as discussed above.

SUMMARY

According to one aspect of the present invention, a flexible conductiveribbon is used to electrically connect a die and an external lead in apackage, such as for power applications and MOSFETs. The connection tothe die is by ultrasonic bonding in one embodiment. Bonding of the leadmay also be by ultrasonic bonding. Other embodiments may utilizethermosonic bonding. The ribbon is of a rectangular cross-section andcan be of a single layer, such as aluminum or copper, or can be ofmultiple layers, such as a thin aluminum bonding layer underlying athicker copper conducting layer. In some embodiments, a single ribbon isused, while in other embodiments, multiple parallel ribbons are bonded.Further, each ribbon can have one or more stitches or bonds on theconductive die surface with one or more loops.

The present invention allows using the same bonding process as withwires, i.e., an ultrasonic bonding process, increasing the cross sectionand contact area for the current paths while limiting or even reducingthe overall volume occupied by the connection, and reducing theprocessing steps and time to produce the connection. Using a ribbon ofthe present invention allows the main loop cross section to be maximizedsince gaps between wires are filled. Even though the ribbon has a largecross section, the thickness can still be reduced compared to a wire,which makes bonding by ultrasonic processes less difficult.Consequently, bonding is easier, the loop height can be lowered, whichresults in lower interconnect height and a potential for reduced packageheight for smaller packages, and the ability to form the loopsincreases, which results in shorter loops and more stitches. Multiplestitches allow using smaller bond areas (per stitch), which alleviatesthe need for a heavy bond head to generate and apply high force andultrasonic power during bonding. Thus, yields higher throughput. The useof multiple stitches, leading to shorter distances between stitches,reduces the spreading resistance, which allows higher current carryingcapability.

In other embodiments, the ribbon can be bonded and cut at differentangles, depending on the orientation of the contacts of the die and leadterminals. This allows optimal usage of the ribbon contact area,maximizes ribbon width, and allows placing a large ribbon in existingpackages designed for round wire bonding (e.g., TO-220 packages) in anoptimized manner.

This invention will be more fully understood in conjunction with thefollowing detailed description taken together with the followingdrawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a side view of a conventional connection between a die anda lead frame using a wire with a single stitch;

FIG. 2 shows a conventional connection between a die and a lead frameusing a strap;

FIGS. 3A and 3B show side and top views, respectively, of a connectionbetween a die and a lead frame according to one embodiment of theinvention;

FIG. 4A is a side view of a connection between a die and a lead frameusing a ribbon with multiple stitches according to another embodiment;

FIG. 4B is a side view of a ribbon with multiple stitches, showingspacing between stitches according to one embodiment;

FIGS. 5A-5C show top views of another embodiment of the presentinvention using multiple parallel ribbons;

FIG. 6 shows a cross-sectional view of a clad ribbon according to oneembodiment of the invention;

FIG. 7 shows a cross-sectional view of a clad ribbon with three layersaccording to another embodiment of the invention;

FIG. 8 shows a portion of a bond tool suitable for ribbon bondingaccording to one embodiment;

FIG. 9A shows a top view of a connection between a die and a lead framewhere the contacts are aligned;

FIG. 9B shows a top of a connection between a die and a lead frame wherethe contacts are not aligned using a conventional process;

FIG. 9C shows a top view of the contact alignment of FIG. 9B using anembodiment of the present invention;

FIG. 10 shows a top view of a device with gate fingers where a ribbonhas stitches between the gate fingers according to one embodiment; and

FIG. 11 shows a side view of stacked ribbons according to an embodimentof the present invention.

Use of the same or similar reference numbers in different figuresindicates same or like elements.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

According to one aspect of the present invention, one or more conductiveflexible ribbons are used to electrically connect a semiconductor die toa lead frame.

FIGS. 3A and 3B show a side view and top view of a semiconductor die 400coupled to a lead frame 402 by a conductive flexible ribbon 404,according to one embodiment of the invention. Die 400 includes ametalized portion 406, such as aluminum, that provides connection tounderlying elements of die 400. Die 400, in one embodiment, is part of apower semiconductor device, such as a power MOSFET. Lead frame 402includes a support portion 407 to which die 400 is secured, e.g., bysolder or epoxy, and terminals 408 that allow electrical connection toexternal devices. An enclosure, covering, or package protects the diefrom external elements. In some embodiments, the semiconductor packageis a TO-220 or an SO-8 package.

Ribbon 404, which may have a rectangular cross section, is aluminum,although other conductive metals, such as copper, are also suitable. Inone embodiment, the mechanical properties of ribbon 404 are similar tothat of wire. For example, a 60 mil×8 mil aluminum ribbon may have atensile strength of approximately 2000 g. The width of ribbon 404 mayrange from 20 mil to 100 mil or more. In one embodiment, the width is120 mil. Larger width ribbons generally are able to replace largernumbers of wires. For example, a single 120 mil ribbon may replace five20 mil wires. The thickness of ribbon 404 may range from 2 mil to 10 milor more. In one embodiment, the thickness is 12 mil. Thicknesses of 2mil require precise cutting control so that the ribbon can be cut whilenot cutting into the substrate. Note that lower thicknesses may bepossible with improved equipment and processes. Some typical sizes ofribbon 404 are 20 mil×2 mil, 20 mil×4 mil, 30 mil×3 mil, 40 mil×4 mil,50 mil×5 mil, 60 mil×8 mil, 80 mil×6 mil, 80 mil×8 mil, 80 mil×10 mil,and 100 mil×10 mil. Aspect ratio (width/thickness), in one embodiment,is between 7 and 13, with a typical ratio of approximately 10. An aspectratio of approximately 10 has been shown to provide a good compromisebetween bondability (the thinner the better) and tilt sensitivity (thethicker the better). Those skilled in the art will appreciate that othersizes of ribbon may also be suitable, depending on factors such assystem requirements and process technology.

Ribbon 404 is bonded to metalized portion 406 by an ultrasonic bondingprocess, as is known by those skilled in the art, and is disclosed,e.g., in commonly-assigned U.S. Pat. Nos. 4,824,005, entitled “Dual modeultrasonic generator in a wire bonding apparatus” to Smith, Jr. and6,439,448, entitled “Large Wire Bonder Head” to Ringler, both of whichare incorporated by reference in their entirety. Ultrasonic bonding ismore environmentally friendly, cleaner, less expensive, and easier tocontrol than soldering. However, ultrasonic bonding becomes moredifficult as the thickness of the wire or ribbon increases. In the caseof a wire, small diameter wires can be used, but a larger number ofwires are needed to obtain the same cross section, thereby resulting inlower productivity and higher cost.

The relatively small thickness of ribbon 404 (e.g., 2 to 10 mil) allowsultrasonic bonding, while a large width (e.g., 20 to 100 mil) allows alarge bonding area. The small thickness of ribbon 404 also providesflexibility so that, within a given area of metalized portion 406, thenumber of bonds or stitches can be increased and the length of ribbonbetween bonds can be decreased. This can be advantageous, as will bediscussed in more detail below.

Referring to FIG. 3B, ribbon 404 is ultrasonically bonded, in oneembodiment, to metalized portion 406 along an area 412, although theactual bond may be smaller. The ultrasonic bonding is by conventionalprocesses, e.g., with frequencies around 60 kHz. However, variations ofcurrent ultrasonic bonding processes are also suitable. For example,ultrasonic bonding can be at a frequency higher than 60 kHz, e.g.,around 80 kHz, which provides higher reproducibility of the resultingbond and requires a smaller vibration amplitude from the bond tool. Inother embodiments, ribbon 404 is thermosonically bonded to metalizationportion 406. There are trade-offs in using thermosonic bonding, such asadditional complexities and costs associated with heating a substrateand bonding on the heated substrate versus lower ultrasonic powerrequirements and a more forgiving process.

Referring back to FIG. 3B, area 412 is approximately the width of ribbon404 and approximately twice the thickness of ribbon 404 in oneembodiment. In other embodiments, the length of area 412 is less thantwice the thickness of ribbon 404, but more than the thickness of ribbon404. In some embodiments, the actual bond from the ultrasonic bonding isat least as large as the area of the cross-sectional area of ribbon 404.A bond tool for a larger (longer) bonded area 412 allows achieving abond of sufficient length (i.e., at least as long as the thickness ofthe ribbon) even with less than optimal ultrasonic bonding parameters.Further, the actual bond area is of the same magnitude as the bond areafor wire bonding, and thus, comparable force (bond) and power capability(ultrasonic) to wire bonding can be used for ultrasonic bonding ribbon404. Typically, sufficient current flow is obtained when the actual bondarea is at least approximately the size of the ribbon's cross section.

In general, performance and processability increase as the width ofribbon 404 increases. However, the width is limited by various factors,such as the ultrasonic bonding process, reliability of the bond, and thetype of package. For example, the width of the ribbon and its aspectratio must be limited depending on the tilt of the bond surface relativeto the bond tool. Stress and strain caused by a thermal expansionmismatch between the ribbon and the substrate increase with increasingsize of the bonded area, progressively limiting the fatigue failurelifetime of a bond with increasing maximum linear dimension. Thecritical linear dimension is the length of the diagonal of therectangular bond area. The severity of this limitation depends on thetype of package and the type of application. It will be less severe in aplastic molded discrete package, but more pronounced in an electronicmodule (which is typically filled with silicon gel only to achieveprotection against oxidation and corrosion). However, as long as themaximum dimension is comparable, e.g., within ±50%, with the maximumdimension of the bond area of a large wire, this limitation is expectedto be comparable to the one for a round wire bond because the largestdimension is still of similar size.

FIG. 4A is a side view showing another embodiment of the presentinvention in which multiple bonds or stitches 500 are used to contactribbon 404 to metalized portion 406. Stitches 500 are formed usingultrasonic bonding in one embodiment. Multiple stitches reduce spreadingresistance along metalized portion 406. As seen from FIG. 4, the shorterthe distance between stitches 500, the less distance current has totravel in the metalization with high electrical resistance, resulting inless spreading resistance and higher current flow to terminals 408 oflead frame 402. In one embodiment, the number of stitches is between 2and 6, although a single stitch may also be used. The distance betweenstitches 500 depends on various factors, such as the size of ribbon 404,the ribbon bonding process, and requirements of the resulting device.For example, thinner ribbons allow the distances to be shorter, due inpart to increased flexibility. In one embodiment, the distance betweenstitches (center-to-center of the stitches) for an 80 mil×8 mil ribbonis between approximately 1.25 mm and 2 mm, and for a 40 mil×4 milribbon, the distance may be reduced down to 0.6 mm.

FIG. 4B is a side view of an embodiment with multiple stitches forillustrating stitch placement on the die. Ribbon 404 is a single wideribbon (approximately the width of metalized portion 406) or one ofmultiple parallel ribbons. Distances x₀, x₁, x₂, x₃, and x₄ are asshown, where x₀+x₁+x₂+x₃+x₄=d (the length of metalized portion 406).Note that only four stitches 500-1 to 500-4 are shown, although othernumbers are also possible. Further, the distances x₀ to x₄ are not shownto scale, as different embodiments will yield different distances. Inone embodiment, the distances x₀ and x₄ (from the center of the stitchesat the ends of the die to the edge of the die) are approximately halfthe distance of the center-to-center distance of the interior stitches,i.e., x₁=x₂=x₃=2x₀=2x₄. Placement in this manner, to a firstapproximation, minimizes the maximum distance between any point onmetalized portion 406 and the nearest bond or stitch 500. Thisapproximation also assumes the resistance of each of the small loops(between stitches 500) is much less than the resistance of the main loop(between stitch 500-1 and terminal 408). The accuracy of theapproximation increases as the number of stitches increases, i.e., adenser placement of stitches.

Among the stitches, resistance is lowest at stitch 500-1, resulting inthe highest current flow and highest current density at stitch 500-1.Thus, in applications that are limited by the peak current, damage mayappear at the first stitch, e.g., in the form of melting of diemetalization and damage of the die due to too high a current density atthe bond or stitch. Consequently, it would be desirable to placestitches 500 such that each stitch “sees” the same resistance or currentflow. Thus, according to another embodiment, stitches 500 are placedsuch that the separation between stitches increases as the stitches movefarther away from terminal 408. In one embodiment, x₀<x₁/2<x₂/2<x₃/2<x₄.

The distance may also be limited by the process in which ribbon 404 isbonded to metalized portion 406. For example, during the bondingprocess, ribbon 404 is fed through a bond tool, as will be described inmore detail below, to the bond area, where ultrasonic bonding securesribbon 404 to metalized portion 406. Additional ribbon 404 is then fedthrough the bond tool to form a loop and down to the next bond area.After the first bond, if the ribbon is looped back from the direction ofthe feed, a shorter distance to the next bond or stitch is possible.However, by looping the ribbon back, stress is placed on the new bond,which may damage or break the bond. Looping the ribbon forward in thesame direction as the feed greatly reduces stress, but also makes theformation of a short loop more critical. In one embodiment, the ribbonis directed at an approximately 90° angle from metalized portion 406,which places a limited level of undue stress on the bond while alsoallowing a short distance between bonds. As will be appreciated by thoseskilled in the art, however, feeding the ribbon forward or backward atvarious angles may be the most desirable depending on the variousfactors such as the bonding equipment, the ribbon, and the devicerequirements.

There are also advantages to minimizing the height H of the ribbonloops. A lower height allows a smaller profile package, as well asreduced resistance for higher current flow. However, as with thedistance limitation, the height is limited by the thickness of theribbon as well as the bonding process. There is no upper limit of theloop height (within the range of typical dimensions of semiconductorpackages or modules), but the lower the target loop height, the morechallenging its control, i.e., to achieve a high reproducibility, theminimum loop height will depend on the thickness of the ribbon (via theinfluence on the stiffness with regards to bending the ribbon). In oneembodiment, loop heights are 1.00 mm (from surface of the die to topsurface of the ribbon) for 8 mil thick ribbons. However, depending ondevice requirements, loop heights can have other heights, such as 0.60mm to achieve reproducibility or sufficient control of the loop heightor 0.40 mm for an 8 mil thick ribbon to allow filling material (e.g.,silicon gel in power modules and plastic mold in discrete power devices)still enough space to properly fill so that voids/bubbles do not formunder the ribbon.

Factors other than device and/or process limitations may also determinethe number of and distance between stitches on metalized portion 406.Even though shorter distances between stitches reduce the resistance andprovide higher current, the larger number of stitches or loops alsodecreases throughput. For applications in which a high current is notcritical, a higher throughput may be more desirable at the cost of lowercurrent flow. In such a situation, a lower number of stitches or bondswould be formed. Therefore, the number of stitches and distance betweenstitches may vary depending on the device requirements.

FIGS. 5A, 5B, and 5C show top views of another embodiment of the presentinvention, in which multiple ribbons 404 are used to connect metalizedportion 406 to terminals 408. FIG. 5A shows four 60 mil×8 mil ribbons404 with three stitches or bonds, FIG. 5B shows four 80 mil×8 milribbons with four stitches, and FIG. 5C shows four 80 mil×8 mil ribbonswith five stitches. Higher current carrying capability or lowerresistance is possible with multiple ribbons since the area from whichthe current to the bond is collected is reduced. In general, as thenumber of ribbons increases, the resistance decreases and current flowincreases. However, as the number increases, the required width of theindividual ribbons can decrease. Narrower ribbons are desirable when thedevice is subject to large temperature variations. This is because asmaller bond experiences less stress from coefficient of thermalexpansion (CTE) effects, resulting in a more reliable bond. Thus,tradeoffs exist between having fewer wider ribbons versus having alarger number of narrower ribbons. As discussed above, a typical aspectratio is approximately 10. Lower aspect ratios may also provideadvantages over wires; however, as aspect ratios decrease (e.g., to 3 orless), the ribbon becomes to look and behave like a wire, therebynegating the advantages provided by ribbons.

Typically, as for a round wire, there is a CTE mismatch between theribbon and the underlying silicon. For example, a copper ribbon may bedesirable because copper has a lower resistance than aluminum and has ahigher melting point. However, when the metalization is aluminum, whichis softer than copper, bonding the copper ribbon to the aluminum layermay result in the bond extending through the aluminum layer and damagingthe underlying silicon (this would be even worse for a round wire, dueto the higher pressure). Therefore, in one embodiment, a copper platingor a metal plate is placed over the metalization layer. The metal plateshould be a material having a CTE between that of silicon and the ribbonmaterial, e.g., copper, to act as a stress/strain buffer. In oneembodiment, the material is nickel-plated molybdenum. This eliminatesthe need to reduce spreading resistance, which results in the resistancemainly residing in the ribbon. A wide copper ribbon with one stitchprovides a large bonding contact area for a reliable bond, whileproviding low resistance for current flow. Further, using a materialhaving a closer CTE to the bond surface (copper) reduces the temperatureeffects on the strength of the bond.

FIG. 6 shows a cross-sectional view of one embodiment of a clad ribbon600 formed from a thin first conductive layer 602 and an overlyingsecond conductive layer 606. First layer 602 is made of the samematerial as the underlying metalization layer 604 to which it is to bebonded. Properties of first layer 602 or bonding layer include increasedbondability (“soft” so that underlying structures remain undamaged andeasily bondable with ultrasonic processes), corrosion resistance, highelectrical conductivity so that current can easy travel through thislayer to reach second layer 606, and relatively low coefficient ofthermal expansion (or near to silicon). In general, the latter twoproperties are somewhat less important than the first two. In oneembodiment, aluminum is used for first layer 602 having a thickness ofapproximately 2 mil. Thus, two like-materials are bonded together (whenthe metalization is aluminum), which results in a stronger and morereliable bond.

Furthermore, since it is currently not possible to directly bond copperto aluminum metalization layers which overlie active circuitry, aluminumbond pads are typically moved to areas where there is no activecircuitry underneath. This can allow bonding of thin (e.g., 2 mil)copper wires to aluminum metalization without the danger of damagingactive elements underneath the aluminum. However, moving bond padsnormally requires making the silicon die larger. Size of the silicon dieis still the major cost factor in a semiconductor device. Therefore, thecapability to bond copper over active circuitry with a high yield isvery desirable, which can be accomplished using a clad ribbon with analuminum layer between the metalization layer and the copper ribbon.

A thicker second layer 606 having higher thermal and electricalconductivities and lower resistance overlies first layer 602. Besideshigh conductivity, second layer 606 should also be corrosion resistantand have a low coefficient of thermal expansion. An additional property,sometimes not as important as the above, is to limit its hardness inorder to not influence loop forming capability too much and to allow agood coupling between the layer and the bond tool. In one embodiment,second layer 606 is copper having a thickness of approximately 6 to 8mil. Second layer 606 can have different thicknesses, depending, in someembodiments, on the thickness of first layer 602 such that the aspectratio is within 7 and 13 (typically 10). Larger cross sections (greaterthickness) will require higher ultrasonic power for bonding andtherefore higher force to reach the necessary coupling between thebonding tool and the copper portion. Copper provides low electricalresistance and/or a strong/stiff and corrosion resistant loop. Othermaterials that may be suitable for second layer 606 include gold, whichis much more costly, and a silver-nickel alloy.

A 2 mil aluminum bonding layer has been found to be suitable withcurrent processes. Aluminum is desirable for ultrasonic bonding becauseit can be joined with many materials at room temperature, is easilybondable, and protects underlying active elements from possible damagefrom ultrasonic bonding. Its “softness” enables bonding to sensitivestructures with high yield. While its electrical and thermalconductivities are high, they are still lower compared to some othermaterials like copper. However, while copper has higher electrical andthermal conductivities, it is relatively hard and difficult to bond.Thus, forming ribbon 600 with a thin aluminum layer between the copperand the aluminum metalization provides advantages of both the copper andthe aluminum. In other embodiments, first layer 602 can be of a metal orbond material similar to but not exactly the same as the underlyingmetalization, which will still yield benefits, although not to theextent of using the same metal. In another embodiment, copper is used.Other embodiments may utilize a harder bonding layer than aluminum, suchas in the case when the metalization underlying the active elements isformed of a harder material, such as copper.

Another design aspect of power interconnects is their reliability.Especially in power modules, the thermal mismatch at the bond interface,mainly caused by the large CTE difference between silicon and aluminumis a limiting factor. Theoretically, this could be drastically changedwith the clad ribbon 600 discussed above, if the main ribbon material orthicker second layer 606 has a CTE nearer to the one of silicon. Forexample, since the CTE of copper (i.e., −17×10⁻⁶ K⁻¹) is nearer to theone of silicon (i.e., −3×10⁻⁶ K⁻¹) than aluminum (i.e., −24×10⁻⁶ K⁻¹) sothat the difference is −14×10⁻⁶ K⁻¹ compared to −21×10⁻⁶ K⁻¹, thereliability should be improved. Calculations have shown an approximatefactor of two improvement. As an example, this offers the potential toimprove the reliability in industrial power modules by approximately afactor two, a long-sought after improvement.

FIG. 7 shows another embodiment of a clad ribbon 700, in which a thirdlayer of material 702 overlies second layer 606. As with the embodimentof FIG. 6, first layer 602 is of a bond material, e.g., conducive toultrasonic bonding, and second layer 606 is of a conductive material,chosen for various aspects such as conductivity and flexibility. As thecoupling between the bond tool and ribbon 700 is another key requirement(which determines the required force to a significant extent), it may bebeneficial to include third layer (or bonding layer) 702, which is notnecessarily identical to first layer 602 at the bottom. Third layer 702would support an optimized coupling between the ribbon and the bondtool. Properties of third layer 702 or coupling layer are selected tohave medium hardness, be corrosion resistant, have high electricalconductivity, and a low coefficient of thermal expansion, althoughtypically the first two properties have greater importance than thelatter two. However, this may change with different applications. In oneembodiment, aluminum is used for third layer 702. Other materials mayinclude copper, gold, and silver, although each has disadvantages. Forexample, copper is hard and gold and silver are more costly. Thethickness of third layer 702, in one embodiment is between approximately0.5 mil and 2 mil, with a typical thickness being 1 mil. First layer 602and second layer 606 are similar to that described above with respect tothe embodiment of FIG. 6.

One advantage of using a ribbon instead of a round wire in a cladconfiguration is that aluminum is more effectively utilized. Forexample, using a round wire with a copper core and an aluminum cylindersurrounding the copper, only the bottom portion of the aluminum is usedfor bonding when the wire is bonded and “flattened” against themetalization. Thus, the upper and side portions of the aluminum are notused to create the bond. However, using a ribbon, the aluminum is fullyutilized during the ultrasonic bonding process. Accordingly, more copper(as a percentage of the total wire cross-section) can be used, resultingin a higher current carrying capability. The thickness of the clad layerof a ribbon can be chosen lower than for a wire (e.g., for a two layeror one-sided clad ribbon), because it has to deform much less (less than1 mil, typically approximately 0.5 mil, according toobservations/investigations).

FIG. 8 shows one embodiment of a portion (the foot) of a bond tool foruse in the present invention. The foot of the bond tool utilizes a crossgroove structure and forms a diamond pattern, as shown. The depth of thegrooves depends on the thickness of the ribbon. In one embodiment, thedepth is between approximately 1.0 mil and 1.5 mil for an 8 mil thickribbon. This pattern type increases the coupling surface between thetool and the ribbon during the bond process. The edges of the groovesalso improve the immediate locking between the tool and the ribbon atthe start of the bond process, reducing the slippage between the tooland the ribbon, and transferring the tool's motion into the ribbon andto the interface between the ribbon and the substrate. It is alsoexpected that this diamond pattern slightly reduces the tilt sensitivityof the ribbon bonding. The bond surface should be well perpendicular tothe bond tool; otherwise the load of the tool onto the ribbon isinhomogeneous, and bonding, then actually over-bonding, takes place onlyon one side of the ribbon. The diamond pattern limits the deformation onthe side where the tool is nearer to the substrate (due to a limitedperpendicularity), but because the tool still easier sinks into thematerial on that side of the ribbon, it will more likely also sink in tosome extent on the other side, and transfer at least some energy. Thus,this type of pattern increases/maximizes contact area between the tooland the ribbon and minimizes damage to the ribbon heel. It has also beenobserved that using ribbons with aspect ratios of 10 provides anacceptable bond quality for tilt angles up to 1°.

In many packages, terminals 408 and metalized portion 406 are “aligned”,as shown in FIG. 9A, along a line 900. Aligned, as used herein, means amajority of the bonding area of terminals 408 are within the areaprojected from the bonding area of metalized portion 406 perpendicularto one of its sides. In these types of packages (e.g., SO-8 packages),ribbon 404 is fed and bonded along line 900 and cut perpendicular toline 900. Here, the maximum width of ribbon 404 is limited by the lesserof the two widths of metalized portion 406 and terminal 408. However,other types of packages may have terminals 408 and metalized portion 406that are offset from each other, such as shown in FIG. 9B. Usingconventional ultrasonic bonding equipment and processes, ribbon 404 isbonded and cut perpendicular to the length of the ribbon, as shown inFIG. 9B. This may reduce the bonding area and width of the ribbon, aswell as the number of stitches or bonds, since the area on terminal 408and metalized portion 406 is not optimally utilized.

FIG. 9C shows one embodiment of the invention in which ribbon 404 is cutand bonded parallel to the intended bond area of terminal 408 andmetalized portion 406. Using this configuration, bonding areas are morefully utilized so that wider ribbons can be used with more bonds.Conventional ultrasonic bonding equipment can be modified so that thebond tool is rotated. This allows the ribbon to be bonded and cut atdifferent angles. By cutting and bonding in parallel with the bondingareas of the die and terminals, the ribbon width, bonding area, and/ornumber of stitches can be advantageously increased. Note thatorientations other than parallel may also provide benefits over bondingwith a fixed tool.

Angle bonding can be accomplished by making modifications to existingultrasonic bonding equipment, such as described in commonly-assignedU.S. Pat. No. 4,976,392, entitled “Ultrasonic wire bonder wire formationand cutter system”, which is incorporated by reference in its entirety.Angle bonding can be achieved by rotating the ribbon guide and thecutter relative to the bond tool or by rotating the bond tool alone(however then the cut is not parallel to the bond (tool)).

One way to achieve an angle bond is by rotating the bond foot of thetool relative to the transducer and wire guide. Although this way theorientation of the tool and therefore the setup is fixed and applicationspecific, it does not mean any other additional effort. Of course thevibration characteristics will be different and a function of the angle,but this can be accommodated for. Also the cutter is rotated if a cutparallel to the bond is required. Such a setup is sufficient in mostdiscrete power applications, where typically only one angle is required(see FIG. 9C). In a power module application, where there may be manymore interconnects under different angles, a flexible solution may berequired. This would allow adjusting the relative angle between bondfoot and ribbon guide and cutter, thereby supporting the flexibility,which is the major strength of ultrasonic bonding compared to otherinterconnect techniques in such applications.

FIG. 10 shows another embodiment of the present invention, in whichribbon 404 with multiple stitches 500 (of FIG. 5) is used with a device,such as a MOSFET die, with gate fingers 1000. Stitches 500 are bondedbetween gate fingers 1000. This eliminates the need to form anadditional insulating layer over fingers 1000. One trend, also in powerelectronics (mainly discrete power MOSFET for DC-DC converterapplications), is to higher switching frequencies. Higher frequencyoperation (e.g., >1 MHz) improves the efficiency in DC-DC converterapplications and allows keeping passive components (e.g., inductors andcapacitors) smaller.

To improve the switching behavior of a MOSFET, gate fingers are designedinto the area of the source metalization (in order to reduce thedistance between the gate and any point in the source to reduce theswitching delay). These gate fingers interrupt the source metalization.For example, U.S. Pat. No. 6,040,626 describes how these fingers need tobe covered with some electrically isolating material such that the clipattached to the source metalization does not create a short between thegate (finger) and the source metalization. If the gate fingerarrangement is such that the stitches of a ribbon can be placed inbetween, the ribbon eliminates the need of this electrical isolationmentioned above.

Using a ribbon in higher frequency applications also provides advantagesof the limited skin effect of ribbons compared to round wires. Forexample, the skin depth at 1 MHz is 3.1 mil for aluminum and 2.5 mil forcopper. Since most of the current flows in a layer underneath theconductor's surface of thickness equal to the skin depth, the reducedcross section results in higher voltage loss and higher Joule heating.For a numerical example, in a 20 mil wire, only the outer ring of 3.1mil thickness carries a significant amount of current. Its cross sectionis

${\left( \frac{\pi}{4} \right) \cdot \left( {20^{2} - 16.9^{2}} \right)} = {90\mspace{14mu} {mil}^{2}}$

or approx. 90/314˜29% of the total wire cross section. In contrast, foran 80 mil×8 mil ribbon, the cross section of the outer ring of 3.1 milthickness (neglecting the short sides) is 2×80 mil×3.1 mil=496 mil² or496/640˜77.5% of the total ribbon cross section.

Although ribbons have been used in other applications, utilizing ribbonsin connection with semiconductor dies and packages, such as high powerapplications and MOSFETs, has not been used for numerous reasons. Forexample, high frequency applications, such as microwave andopto-electronic, use ribbons for its improved high frequency capability.The rectangular cross section reduces the skin effect, low loops ofappropriate shape result in low inductance of the interconnect, and theshape is more similar to the one of strip lines, resulting in lowerreflection losses at the ends of the interconnect. High frequencyapplications desire ribbons that have large surface area (reducing skineffects) and loops with well defined geometry (small variance ininductance). This leads to single ribbons with single bonds, sincespreading resistance is not an issue. Furthermore, ribbons used in thesehigh frequency applications typically use gold as the ribbon materialand processes the bonds with heating the substrate, i.e., it is athermosonic process and not a pure ultrasonic process (i.e., withoutapplication of heat).

The use of ribbon bonding of the present invention yields numerousadvantages. The extent of the productivity/throughput improvement willdepend on the application. For example, in a medium power package (e.g.,a TO-220 package), three parallel 20 mil aluminum wires with twostitches on the die each were replaced with one 80 mil×10 mil aluminumribbon with three stitches on the die, for equal electrical performance.The productivity improvement increased by a factor of approximately 2.5,as the process time for such a ribbon with the design criteria (withregards to the size of the bond area) described is comparable to that ofa single 20 mil wire. In a low power package (e.g., an SO-12 package),four 5 mil aluminum wires with a single stitch on the die were replacedwith one 30 mil×3 mil aluminum ribbon with a single stitch on the die.The productivity improvement factor is approximately 4, as the processtime for such a ribbon is comparable to that of a single 5 mil wire.

The present invention provides other features that may be beneficial.For example, ribbon bonding yields a higher stiffness in the substrateplane, thereby lowering sensitivity to vibrations in that direction.This may have advantages in automotive applications, where silicon gelused to fill the power modules exerts a significant force on wires undervibration. Other advantages may result from replacing multiple wireswith a single ribbon or lower number of ribbons. For example, it iscommon to pull-test wires after bonding to determine the quality of thebond. As the number of wires on a die increases, the time to pull-testall the wires on the die increases and/or the number of pull-testdevices needed increases. Consequently, if a single ribbon or lowernumber of ribbons are used instead of wires, time and/or costs maydecrease. Also, by reducing the number of total bonds or stitches on thedie, a lower yield loss potential is possible due to lower chances offorming a faulty or damaging bond on the die. It was also observed thatdue to the lower pressure, an aluminum ribbon does not penetrate as deepinto the metalized area of a die, generally <1 micron, compared to around wire of comparable hardness (>1 micron, depending on diameter andhardness). This too reduces the risk of damage to the underlyingcircuitry, offering the potential of a lower yield loss, and thereforeof lower cost of manufacturing.

Another improvement potential the rectangular ribbon geometry offerscompared to the round wire geometry is the ability to stack severalribbons on their bonds/stitches over each other, as shown in FIG. 11.Three ribbons 404 are shown stacked on stitches 500. Each subsequentlystacked ribbon is bonded, e.g., ultrasonically, to a correspondingunderlying bond or stitch 500. This allows the interconnect crosssection to be further increased, while still keeping the heightcomparable that of a wire. For example, up to three 80 mil×8 mil ribbonscan be stacked this way in a power module application. With the trend tomore efficient power semiconductors, die size is decreasing whilecurrent capability remains constant or even increases. This requireslarger cross section interconnects. If the width cannot be increasedand/or the aspect ratio must be kept at a specific value, stacking willstill allow to increase the interconnect cross section. With the presentcutting system, the last stitch 500-3 cannot be stacked, as the systemneeds a support underneath the tool during the cut move, and thereforethere would not be sufficient space in a discrete power package for thismethod. However this limitation could be overcome with an appropriatedesign of the cut mechanism. Note that this aspect of the invention doesnot require stacking on ribbons with multiple stitches; stacking overribbons with a single bonded stitch also provides advantages, asdiscussed above.

The above-described embodiments of the present invention are merelymeant to be illustrative and not limiting. It will thus be obvious tothose skilled in the art that various changes and modifications may bemade without departing from this invention in its broader aspects. Forexample, the bonding of a semiconductor die to a package is describedabove. However, ribbon bonding can also be between two elements in anelectronic module, of which one, both, or none are a semiconductor die.Further, the bonding is described primarily with regards to ultrasonicbonding, and to a lesser degree, thermosonic bonding. However, otherboding processes that are suitable for use with the flexible ribbondiscussed herein may also be used, such as thermocompression. Bondingmay be the of the same or different types for both die-to-ribbon andlead-to-ribbon. Therefore, the appended claims encompass all suchchanges and modifications as fall within the true spirit and scope ofthis invention.

1. A method of providing an electrical interconnection between a firstelement and a second element, the method comprising the steps of: a)ultrasonically bonding a first portion of a ribbon material to a firstelement using a bonding tool, the ribbon material having a rectangularcross section; b) extending a length of the ribbon material, continuouswith the first portion, to a second element after step a); and c)bonding a second portion of the ribbon material to the second elementusing the bonding tool, thereby providing an electrical interconnectionbetween the first element and the second element.
 2. The method of claim1, wherein the ribbon material having the rectangular cross section isprovided such that a ratio of a width of the ribbon material to athickness of the ribbon material is in a range of 7-13.
 3. The method ofclaim 1, wherein step a) includes ultrasonically bonding the firstportion of the ribbon material to a semiconductor die supported by asubstrate.
 4. The method of claim 3, wherein the substrate is aleadframe, and step c) includes bonding the second portion of the ribbonmaterial to a lead of the leadframe.
 5. The method of claim 1, whereineach of the first element and the second element comprise asemiconductor die.
 6. The method of claim 1, wherein extending thelength of the ribbon material includes feeding the length of the ribbonmaterial after step a).
 7. The method of claim 6, wherein the feedingthe length of the ribbon material includes guiding the length of theribbon material with a ribbon guide.
 8. The method of claim 1, furtherincluding the step of: d) cutting the ribbon material after step c). 9.The method of claim 1, wherein step b) includes extending the length ofthe ribbon material such that the length follows an arc shape.
 10. Themethod of claim 1, wherein step a) includes ultrasonically bonding thefirst portion of the ribbon material to the first element such that thefirst portion of the ribbon material includes a first bonded portion, asecond bonded portion, and a third bonded portion.
 11. The method ofclaim 10, wherein step a) includes forming a first loop of the ribbonmaterial between the first bonded portion and the second bonded portion,and forming a second loop of the ribbon material between the secondbonded portion and the third bonded portion.
 12. The method of claim 1,wherein step a) includes ultrasonically bonding the first portion of theribbon material to the first element such that the first portion of theribbon material includes a first bonded portion, a second bondedportion, and a third bonded portion, the first bonded portion beingclosest to the second element in comparison to a position of the secondbonded portion and the third bonded portion, the second bonded portionbeing positioned between the first bonded portion and the third bondedportion, wherein when measured in a direction along which the ribbonmaterial extends (1) a distance between a centerline of the secondbonded portion to a centerline of the first bonded portion is less than(2) a distance between a centerline of the third bonded portion to acenterline of the second bonded portion.
 13. An electricalinterconnection between a first element and a second element, including:a first portion of a ribbon material ultrasonically bonded to a firstelement, the ribbon material having a rectangular cross section; alength of the ribbon material, continuous with the first portion,extending to a second element spaced apart from the first element; and asecond portion of the ribbon material bonded to the second element. 14.The electrical interconnection of claim 13, wherein the first elementcomprises a semiconductor die, and the second element comprises asubstrate supporting the semiconductor die.
 15. The electricalinterconnection of claim 13, wherein each of the first element and thesecond element comprise a semiconductor die.
 16. The electricalinterconnection of claim 13, wherein the ribbon material having therectangular cross section has a ratio of a width of the ribbon materialto a thickness of the ribbon material in a range of 7-13.
 17. Theelectrical interconnection of claim 13, wherein the length of ribbonextending to the second element follows an arc shape.
 18. The electricalinterconnection of claim 13, wherein the ultrasonically bonded firstportion includes a plurality of stitch bonds.
 19. The electricalinterconnection of claim 13, wherein the ultrasonically bonded firstportion includes from about 2 to 6 stitch bonds.
 20. The electricalinterconnection of claim 13, wherein the first portion of a ribbonmaterial ultrasonically bonded to the first element includes a firstbonded portion, a second bonded portion, and a third bonded portion. 21.The electrical interconnection of claim 20, wherein the first portion ofthe ribbon material ultrasonically bonded to the first element includesa first loop having a first height between the first bonded portion andthe second bonded portion, and a second loop having a second heightbetween the second bonded portion and the third bonded portion.
 22. Theelectrical interconnection of claim 13, wherein the first portion of aribbon material ultrasonically bonded to the first element includes afirst bonded portion, a second bonded portion, and a third bondedportion, the first bonded portion being closest to the second element incomparison to a position of the second bonded portion and the thirdbonded portion, the second bonded portion being positioned between thefirst bonded portion and the third bonded portion, wherein when measuredin a direction along which the ribbon material extends (1) a distancebetween a centerline of the second bonded portion to a centerline of thefirst bonded portion is less than (2) a distance between a centerline ofthe third bonded portion to the centerline of the second bonded portion.